| SPEC |
Diameter
(mm) |
Tolerance
(mm) |
Tensile Strength
(N/mm2) |
Reduction of
Area
(%) |
Depth of Flaw
(mm) |
Decarburized Depth
(mm) |
Winding /
Bending |
JIS G3560
SWOSC-B
&
JIS G3561
SWOSC-V |
1.00 |
+/- 0.02 |
1960 - 2110 |
45↑ |
0.01 mm↓ |
Dia * 1.5%
↓ |
Winding
Test |
1.20 |
+/- 0.02 |
1960 - 2110 |
45↑ |
1.40 |
+/- 0.02 |
1960 - 2110 |
45↑ |
1.60 |
+/- 0.02 |
1960 - 2110 |
45↑ |
1.80 |
+/- 0.02 |
1960 - 2110 |
45↑ |
2.00 |
+/- 0.02 |
1910 - 2060 |
45↑ |
2.30 |
+/- 0.02 |
1910 - 2060 |
45↑ |
Dia * 0.5%
↓ |
2.60 |
+/- 0.02 |
1910 - 2060 |
45↑ |
2.90 |
+/- 0.02 |
1910 - 2060 |
45↑ |
3.00 |
+/- 0.02 |
1860 - 2010 |
45↑ |
3.20 |
+/- 0.02 |
1860 - 2010 |
40↑ |
3.50 |
+/- 0.03 |
1860 - 2010 |
40↑ |
0.05 mm↓ |
4.00 |
+/- 0.03 |
1860 - 2010 |
40↑ |
4.50 |
+/- 0.03 |
1810 - 1960 |
40↑ |
5.00 |
+/- 0.03 |
1760 - 1910 |
40↑ |
5.50 |
+/- 0.03 |
1760 - 1910 |
35↑ |
5.60 |
+/- 0.03 |
1710 - 1860 |
35↑ |
6.00 |
+/- 0.04 |
1710 - 1860 |
35↑ |
6.50 |
+/- 0.04 |
1710 - 1860 |
35↑ |
Dia * 0.7%
↓ |
Bending
Test
(90°) |
7.00 |
+/- 0.04 |
1710 - 1860 |
35↑ |
7.50 |
+/- 0.04 |
1710 - 1860 |
35↑ |
8.00 |
+/- 0.04 |
1710 - 1860 |
30↑ |
8.50 |
+/- 0.04 |
1710 - 1860 |
30↑ |
9.00 |
+/- 0.05 |
1710 - 1860 |
30↑ |
9.50 |
+/- 0.05 |
1710 - 1860 |
30↑ |
10.0 |
+/- 0.05 |
1710 - 1860 |
30↑ |
10.5 |
+/- 0.07 |
1710 - 1860 |
30↑ |
11.0 |
+/- 0.07 |
1710 - 1860 |
30↑ |
11.5 |
+/- 0.07 |
1710 - 1860 |
30↑ |
12.0 |
+/- 0.07 |
1710 - 1860 |
30↑ |
13.0 |
+/- 0.07 |
1660 - 1810 |
30↑ |
14.0 |
+/- 0.07 |
1660 - 1810 |
30↑ |
15.0 |
+/- 0.07 |
1660 - 1810 |
30↑ |
16.0 |
+/- 0.07 |
1660 - 1810 |
30↑ |
17.0 |
+/- 0.07 |
1660 - 1810 |
30↑ |
|
|
|
 |