| 一、Galvanized Wire for Packing |
| |
Diameter
(mm) |
Tolerance
(mm) |
| ≦3.00 |
± 0.05 |
| ≧3.01 |
± 0.06 |
|
|
Diameter
(mm) |
Zinc Value
(g/m2) |
Tensile Strength
(kg/mm2) |
| 2.00~2.80 |
140 |
130 |
| ≧2.81 |
135 |
140 |
|
|
Diameter
(mm) |
Torsion
(times) |
Bending
(times) |
2.00~3.00 |
10 |
8 |
3.01~4.00 |
10 |
7 |
|
| |
| 二、Galvanized Wire for Suspension of Electrical Cable Wire |
| |
|
Diameter
(mm) |
Tolerance
(mm) |
Breaking Load
(kg) |
Tensile Strength
(kg/mm2) |
Torsion
(100*D) |
Zinc Value
(g/m2) |
Wrapping
(8*D) |
Uniformity |
times/60s |
times/30s |
2.15 |
± 0.04 |
544 |
150 |
16 |
200 |
6 |
2 |
--- |
2.48 |
± 0.04 |
724 |
150 |
16 |
250 |
6 |
2 |
1 |
2.70 |
± 0.04 |
858 |
150 |
16 |
250 |
6 |
2 |
1 |
2.80 |
± 0.04 |
923 |
150 |
16 |
250 |
6 |
3 |
--- |
|
| |
| 三、Galvanized Wire for Patenting |
| |
Spec. |
82B |
72B |
62B |
62A |
57A |
52A |
42A |
Diameter Tolerance (mm) |
± 0.06 |
± 0.06 |
± 0.06 |
± 0.06 |
± 0.06 |
± 0.06 |
± 0.06 |
Tensile Strength (kg/mm2)
|
105~135 |
95~125 |
85~115 |
80~110 |
75~110 |
70~105 |
68~98 |
Elongation(%) |
6.0 |
Torsion (times) |
15 |
Zinc Coating(g/m2) |
150 |
|
| |
| 四、A.C.S.R. |
| |
Composition |
Ｃ |
Ｍｎ |
Ｐ |
Ｓ |
Ｓｉ |
Contents % |
0.53~0.86 |
0.3~0.9 |
＜0.035 |
＜0.035 |
0.15~0.35 |
|
| |
Diameter
(mm) |
Tolerance
(mm) |
Tensile Strength
Class A (kg/mm2) |
Elongation
Class
(%) |
Zinc Value Class
(g/m2) |
Primary Loading
(kg/mm2) |
Elongation Setting
(%) |
(kg/mm2) |
1% of Elongation |
1.270~1.521 |
+ 0.038
- 0.025 |
148 |
137 |
3.0 |
183 |
10.2 |
0.05 |
1.524~1.902 |
198 |
1.905~2.283 |
+ 0.051
- 0.025 |
214 |
2.286~2.639 |
144 |
131 |
3.5 |
229 |
19.4 |
0.10 |
2.642~3.045 |
244 |
3.048~3.553 |
+ 0.076
- 0.051 |
144 |
127 |
4.0 |
259 |
29.6 |
0.15 |
3.556~4.569 |
+ 0.102
- 0.076 |
141 |
120 |
4.0 |
274 |
4.572~4.822 |
305 |
|
| |